- Electrotransport of Carbon and Nitrogen in γ-Iron
- ガンマ Feチュウ ノ C N ノ エレクトロトランスポート
- Electrotransport of Carbon and Nitrogen in γ-Iron
この論文をさがす
抄録
The effective valences Z∗ and the non-dimensional number δ of carbon and nitrogen in γ-iron for the solid state electrotransport have been measured by the tangent method under the following conditions: electric field intensity=3.0-11.3 V·m−1, temperature=1223-1323 K, initial carbon content=0.1-0.9 mass% and nitrogen content=0.025 mass%. The influences of these factors on Z* and δ were examined, and the following results were obtained:<BR>(i) At the electric field intensity below 5.0 Vm−1, Z∗ of carbon increased rapidly with decreasing electric field intensity, but δ kept constant. Above that value, Z∗ of carbon was constant, and δ increased linearly with increasing electric field intensity.<BR>(ii) Temperature did not influence Z∗ and δ of carbon under the present experimental conditions.<BR>(iii) Z∗ and δ of carbon decreased gradually with increasing concentration of carbon.<BR>(iv) Z∗ of carbon and nitrogen increased slightly when both elements coexisted.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 59 (12), 1247-1252, 1995
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681468126208
-
- NII論文ID
- 130007341973
- 10001672013
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3641582
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可