The effects of deformation and pre-aging on age-hardening of Al-Mg2Si alloys containing 0.4mass% excess silicon were investigated by Vickers micro-hardness test and transmission electron microscope observation. The time required to reach a maximum value of age-hardening curve (tmax) was shortened by deformation just prior to aging for all alloys. The maximum hardness value (Hmax) increased with increasing the amount of deformation in an 0.4%Mg2Si alloy aged at 473K. The precipitates became finer by the deformation prior to aging. The Hmax, values were independent of the amount of deformation and were constant for alloys containing Mg2Si ranged from 0.6 to 1.0%. For those alloys, the size of precipitates was larger and the number of precipitates was reduced by the addition of deformation. The tmax at 473K was shortened by pre-aging at 423K before deformation in an 0.6%Mg2Si alloy. The pre-aging and deformation treatment has also the effect to increase the Hmax to a higher value equivalent to that obtained by the conventional aging at 423K.
収録刊行物
-
- 軽金属
-
軽金属 45 (2), 95-100, 1995
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681313766656
-
- NII論文ID
- 10001724606
- 10003795701
- 10003904246
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK2MXksF2jtL8%3D
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 3601765
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可