- Microstructure and Mechanical Properties of TiAl-Ti2AlC Composites Produced by Combustion Reaction Process.
- ネンショウ ハンノウ プロセス ニ ヨリ サクセイシタ TiAl Ti2AlC
この論文をさがす
抄録
To enhance the negligible low-temperature ductility and low high-temperature strength of titanium aluminides, TiAl-Ti2AlC composites were made by the combustion reaction process, following arc-melting. The alloy compositions included Ti52Al43C5, Ti50Al45C5 and Ti48Al47C5 in at%. The resulting composites had about l8vol%Ti2AlC in the matrix TiAl with a lamellar structure of Ti3Al. In the annealed specimens, smaller particles were visible in the matrix, and appeared to form in place of solutionizing lamellae. Therefore, carbon atoms in the matrix, probably in the Ti3Al phase, formed carbide Ti2AlC particles with the smaller sizes. On the other hand, the behavior with regard to change in lattice parameters and Vickers hardness suggested a reduction in the solubility of carbon in the TiAl phase with decrease in annealing temperature. For the Ti50Al45C5 alloy, annealed at 1273K, ambient-temperature ductility up to 0.9% was achieved in bending.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 42 (11), 1289-1294, 1995
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206308957824
-
- NII論文ID
- 10001750252
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DyaK28XhvFGltg%3D%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 3642101
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可