- Effect of Small Quantity of Oxygen and Nitrogen on Mechanical Properties of New Titanium Alloys for Medical Implants
- セイタイヨウ シン Ti ゴウキン ノ キカイテキ セイシツ ニ オヨボス サ
この論文をさがす
抄録
The combined effect of O and N additions on the fatigue properties with Ti-15%Zr-4%Nb-4%Ta-0.2%Pd-0.2%O-0.05%N and Ti-15%Sn-4%Nb-2%Ta-0.2%Pd-0.2%O alloys were investigated by fatigue testing in a physiological saline solution at 310 K. The fatigue test was carried out under the condition of a tension to tension mode with a sine wave at a stress ratio of 0.1 and at a frequency of 2 Hz and 10 Hz in Eagle’s medium solution using an environment cell with 90%N2+5%CO2+5%O2 gas bubbling. Further the effect of human hip joint load profile estimated by analysis of forces and actions for human hip joint on the corrosion fatigue strength were examined.<BR>The effect of heat treatment on the mechanical strength of the new Ti alloys were investigated. As the solution treatment temperature increased the ductility of Ti-Zr and Ti-Sn alloys decreased. After solution treatment, the mechanical strength of Ti-Zr and Ti-Sn alloys did not change much as the aging time and the aging temperature increased. The additions of O and N to the new Ti alloys and heat treatment substantially increased the ultimate tensile strength to 1000 MPa. Also, the total elongation was more than 10%. The fatigue strength of Ti-Sn alloy added 0.2%O, 0.005%N and Ti-Zr alloy added 0.2%O, 0.05%N at 108 cycles was 1050 MPa and 950 MPa, respectively. The effect of frequency on the fatigue strength at 2 Hz and 10 Hz was almost similar. Moreover, the fatigue strengths ware almost the same for sine wave and human hip joint load profile in both Ti-Zr and Ti-Sn alloys.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 62 (2), 207-214, 1998
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681468292992
-
- NII論文ID
- 10001969178
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214876
-
- NDL書誌ID
- 4413812
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可