磁性材料の化学　焼結１８Ｃｒ‐２Ｍｏ‐Ｆｅ合金の交流磁気特性

• 加藤 哲男

  大同工業大学

• 倉田 規義

  大同工業大学大学院工学研究科

• 富岡 雄

  大同工業大学

• 草加 勝司

  大同特殊鋼(株)技術開発研究所

書誌事項

タイトル別名

• AC Magnetic Property of the Sintered 18Cr-2Mo-Fe Alloy.
• ショウケツ 18Cr 2Mo Fe ゴウキン ノ コウリュウ ジキ トクセイ

抄録

Influence of the silicon content on the AC magnetic property was studied on the sintered 18Cr-2Mo-Fe magnetic alloy. The highest DC and AC magnetic properties were attained at the content of two-percent silicon. The lowering of the properties was observed at the three-percent silicon or above. The density and the DC magnetic property of sintered alloy was improved with the rise of sintering temperature, but the AC magnetic property indicated a decrease after an increase. This may be attributed to the change of the electrical resistivity originated in the porosity. The highest DC magnetic property and the increase of electrical resistivity are believed to be caused by the improvement of AC magnetic property at the content of two-percent silicon. The lowering of AC magnetic property above three-percent silicon may be due to the decrease of density resulted from the decrease of the press-compatibility.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 43 (1), 72-77, 1996

  一般社団法人 粉体粉末冶金協会

キーワード

• FeCr sintered magnetic alloy
• AC magnetic property
• Silicon content
• Sintered density
• Resistivity

詳細情報

• CRID: 1390282681286070272
• NII論文ID: 10002011095
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.43.72
• COI: 1:CAS:528:DyaK28XhtlGhurY%3D
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 3918037
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3918037
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可