酸化物超伝導体の合成と特性　ＢａＯ（ＢａＣＯ３）‐ＣａＯ‐ＣｕＯ系における生成相と相関係

• 草野 圭弘

  倉敷芸術科学大学芸術学部

• 菊池 丈幸

  岡山大学工学部

• 高田 潤

  岡山大学工学部

• 池田 靖訓

  京都大学化学研究所

• 高野 幹夫

  京都大学化学研究所

• 坂東 尚周

  京都大学化学研究所

書誌事項

タイトル別名

• Phases and their Relations in the BaO(BaCO3)-CaO-CuO System.
• BaO BaCO3 CaO CuOケイ ニ オケル セイセイソウ ト ソウ カ

抄録

Phases and their relations in the BaO(BaCO₃)-CaO-CuO system at 900°C in air have been studied by XRD. The formation of two types of copper oxycarbonates were newly formed: one is a phase with a composition of Ba:Ca:Cu=0.600:0.080:0.320 and the other is a solid solution formed in a region of the compositional triangle of (Ba:Ca:Cu)=(0.666:0:0.333)-(0.650:0.017:0.333)-(0.650:0.070:0.280). The crystal structures of these phases have been determined by XRD, TEM and ED. These copper oxide carbonates commonly have tetragonal structures with a≈√2a_p and c≈2a_p. Unfortunately, no diamagnetic response was observed for the new two copper oxycarbonates.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 43 (2), 157-161, 1996

  一般社団法人 粉体粉末冶金協会

キーワード

• BaO(BaCO<SUB>3</SUB>)-CaO-CuO system
• phase diagram
• new copper oxycarbonate
• TEM image
• susceptibility

詳細情報

• CRID: 1390001206307390208
• NII論文ID: 10002011230
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.43.157
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 3926711
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3926711
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可