- Effects of Addition of Oxide Particles on Formation and Superconducting Properties of the Bi-2212 Phase.
- Bi 221 2ソウ エ ノ サンカブツ リュウシ テンカ コウカ
この論文をさがす
抄録
Bi-2212/Ag tape samples with finely dispersed oxide(x-Al2O3 or MgO) particles were prepared by the partial melt-solidification technique. The formation and superconducting properties of the tape samples have been studied in relation to microstructure. In case of a-Al2O3 particles addition, as the oxide additive content increased, the Ic value at 77K and OT decreased remarkably because of reaction between a-Al2O3 and 2212 phase. On the other hand, MgO particles were uniformly dispersed in the Bi-2212 matrix without any reaction between 2212 phase and MgO, so that Ic almost unchanged. Isothermal magnetic hysteresis loop of MgO added samples was larger than that of non-added samples. These results suggested that MgO particle addition was effective for improvement in the flux pinning properties of the Bi-2212 phase.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 43 (2), 183-186, 1996
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206307391488
-
- NII論文ID
- 10002011282
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3926715
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可