アーク溶解法によるB-C系固溶体の作製とその熱電性能 Preparation of B-C System Solid Solutions by Arc Melting and their Thermoelectric Properties

この論文にアクセスする

この論文をさがす

著者

抄録

B-C system compounds were prepared by arc melting in argon atmosphere using B<SUB>4</SUB>C, B and C powders. The non-stoichiometric composition of the B-C compounds ranged between 10 and 20at%C. The maxima of the Seebeck coefficient values were observed at 20at%C (B<SUB>4</SUB>C), and the greatest value was 270 μV/K at 1100K. The electrical conductivity increased with increasing carbon content in general, but had minimum at 17at%C (B<SUB>5</SUB>C). The thermal conductivity increased with increasing carbon content. The thermoelectric figure of merit values (Z) decreased with increasing carbon content, but the Z values showed maximum at 20at%C (B<SUB>4</SUB>C). The greatest ZT value of B<SUB>4</SUB>C at 1100K was 0.15.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 43(3), 306-310, 1996-03-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  16件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  2件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002011554
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    3936695
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ