Si-Ti-C-O系繊維の表面構造がセラミック複合材料の特性に及ぼす影響 Effect of Surface Structure of Si-Ti-C-O Fiber on Properties of Ceramic Matrix Composite

この論文にアクセスする

この論文をさがす

著者

抄録

Ceramic matrix composites using three dimensional woven fabric of Si-Ti-C-O fiber were fabricated by infiltration of polytitanocarbosilane solution and pyrolysis, and evaluated. It was possible to fabricate a dence composite even by this convenient method. The composite using Si-Ti-C-O fiber which has both of oxide rich surface layer and carbon rich surface layer, was excellent in mechanical property compared to the composites using Si-Ti-CO fiber with carbon rich surface layer or with no surface layer. The composite using Si-Ti-C-O fiber with two surface layers maintained about 80% of bending strength after heat-treatment at 1200°C for 100 hours in air.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 43(3), 353-357, 1996-03-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  5件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  2件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002011705
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    3936704
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ