SiC whisker reinforced MoSi2 composites were fabricated by hot pressing to more than 98% of theoretical density. Flexural strength and steady state creep strain rate of these composites exhibited substantial improvements over MoSi2 matrix material. In the case of the MoSi2-20vol% SiC whisker composites, the flexural strength was 1010 MPa (2.8 times MoSi2 matrix) at room temperature and 1420 MPa (3.7 times MoSi2 matrix) at 1000°C; the steady state creep strain rate under a stress of 100 MPa at 1300°C was 2.2×10-7/Sec (1/26 of MoSi2 matrix). The material and microstructural characteristics contributing to these improvement mechanisms are discussed in this paper.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 43 (4), 444-449, 1996
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206307784704
-
- NII論文ID
- 10002011867
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3954805
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可