- Thermoelectric Properties of FeSi2 with SiC Dispersion Prepared by Mechanical Alloying.
- MAホウ ニ ヨリ SiC オ ブンサンシタ FeSi2 ノ ネツデン トクセ
この論文をさがす
抄録
Thermoelectric properties of β-FeSi2 with SiC dispersion prepared by mechanical alloying were investigated. The FeSi2 alloys doped with Mn or Co (p-type Fe0.92Mn0.08Si2, n-type Fe0.98Co0.02Si2) were prepared by arcmelting in Ar. Mixtures of these FeSi2 alloys with Si+C powders were mechanically alloyed for 72ks, and hot pressed at 1173K for 3.6ks under 25MPa. XRD showed that β-FeSi2 and SiC were formed during hot pressing Si+C addition had little influence on the thermoelectric power of β-FeSi2. On the other hand, the resistivity increased with increasing Si+C addition. The thermal conductivity drastically decreased by about 30% with increasing Si+C addition in all temperature range. This is considered to be due to the SiC dispersion in β-FeSi2. SiC phase restrained the growth of β-FeSi2 phase and phonons scattering at grain boundaries increased, therefore thermal conductivity decreased. SEM photographs showed that 10-20μ m SiC particles dispersed in the β-phase. The figure of merit, Z=α2/(ρ⋅k), where α : thermoelectric power, ρ : resistivity, K : thermal conductivity, of Fe0.92Mn0.08Si2 added 5wt.% Si+C is higher than that of Fe0.92Mn0.08Si2 without Si+C addition. As a result, it is effective to add Si+C to p-type Fe0.92Mn0.08Si2.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 43 (5), 608-612, 1996
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681284213376
-
- NII論文ID
- 10002012174
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3967169
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可