Magnetic Properties of Nd-Fe-B Magnets Sintered Using Granulated Powders by Spray Drying Method (II).
-
- Yamashita Osamu
- Reserch & Development Department, Sumitomo Special Metals Co., Ltd.
-
- Kishimoto Yoshihisa
- Advanced Technology Research Laboratories, Sumitomo Metal Industries, Ltd.
Bibliographic Information
- Other Title
-
- スプレー造粒粉を用いたNd‐Fe‐B焼結磁石の磁気特性 II
- スプレーゾウリュウ フン オ モチイタ Nd Fe B ショウケツ ジシャク
Search this article
Abstract
Nd-Fe-B alloy powder was granulated by spray drying method using methylcellulose (MC) binder in the range from 0.1 to 0.5wt%, in order to improve the powder flowability during feeding and compacting. After adding MC binder, glycerin and pure water to alloy powder, the slurry was stirred at 278K in N2 atmosphere to suppress the oxidation of alloy powder. The granulated powders with MC binder exhibited higher flowability than granulated powders with polyvinylalcohol(PVA) binder. By heating in H2 at 673K after compacting in a magnet field, 96% of carbon in binder was removed, although the oxygen in binder remained unremoved. With the compacted body added 0.20wt% MC, these treatments can allow to suppress the residual contents of oxygen and carbon in the resulted sintered magnets within less than 8500ppm and 600ppm, respectively. The coercive force(iHc) and maximum energy product (BH) max for a sintered anisotropic magnet prepared by the above mentioned process are 0.96(MA/m) and 241.1 (kJ/m3), respectively, in which (BH)max is lower by 15% than that obtained by using PVA binder.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 43 (5), 675-681, 1996
Japan Society of Powder and Powder Metallurgy
- Tweet
Details
-
- CRID
- 1390282681284219136
-
- NII Article ID
- 10002012317
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 3967180
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed