Magnetic Properties of Sm3(Fe, Co, M)29NY Compounds(M=V, Cr).
-
- Yamamoto Hiroshi
- School of Science and Technology, Meiji University
-
- Takahashi Kashu
- School of Science and Technology, Meiji University
-
- Tomii Kazuya
- School of Science and Technology, Meiji University
Bibliographic Information
- Other Title
-
- Sm3(Fe,Co,M)29NY化合物(M=V,Cr)の磁気特性
- Sm3 Fe Co M 29NY カゴウブツ M V Cr ノ ジキ トクセイ
Search this article
Abstract
An experiment was carried out to investigate the magnetic and physical properties of Sm3(Fe0.81Co0.10V0.09)29Nr and Sms(Fe0.75Co0.10Cr0.15)29Ny compounds. These compounds were prepared by nitrogenation of Sn (Fe0.81Co0.10V0.09)29 and Sm3(Fe0.75Co0.10Cr0.15)29 alloy powders (about 30μm) in high-purity nitrogen gas at pressure of 4.9MPa, and temperatures of 475-600°C for 0.5-5h. Sm3(Fe0.75Co0.10Cr0.15)29Ny alloy powders get a high coerrivily after nitrogenation. It was found when Sm3(Fe0.75Co0.10Cr0.15)29Nr powders were subsequently heated at 500-600°C for 3-25h under 98kPa of argon atmosphere, the value of coercivity of this compounds increased. The conditions determined as optimum for preparing the powders with best values of σs=139.5×10-6Wb-rndkg, HcJ=332kA/m, HA= 4.62MA/m, and Tc = 563.9t, are as follows: nitrogenation ; 600°C×1h, heat treatment ; 5501×10h. These powders were found to absorb approximately 7-8atoms of nitrogen per unit formula.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 43 (8), 1019-1024, 1996
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001206307702912
-
- NII Article ID
- 10002012877
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 4012527
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed