ＰＺＴ系圧電体の焼結挙動に及ぼすＮｂ２Ｏ５とＭｎＯの添加効果

• 山川 孝宏

  日本セメント(株)中央研究所

• 片岡 昌子

  日本セメント(株)中央研究所

• 江崎 徹

  日本セメント(株)中央研究所

• 高橋 繁

  日本セメント(株)中央研究所

• 井上 嘉和

  日本セメント(株)中央研究所

書誌事項

タイトル別名

• Influence of Nb2O5 and MnO Dope on the Sintering Behavior of PZT Ceramics.
• PZTケイ アツデンタイ ノ ショウケツ キョドウ ニ オヨボス Nb2O5

抄録

The mechanism of shrinkage during sintering was investigated on PZT ceramics. Nb₂O₅ and MnO was added to PZT calcined powder. The mechanism of shrinkage was determined from the shrinkage-time curves. The mechanism of shrinkage and grain growth changed depending on the Nb₂O₅/MnO ratio. The dominant mechanism was volume diffusion when the Nb₂O₅/MnO ratio was larger than 6. On the other hand, the volume diffusion was inhibited when the Nb₂O₅/MnO ratio was less than 4. The grain growth was inhibited in the former conditions, while it was promoted in the latter conditions.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 43 (9), 1132-1135, 1996

  一般社団法人 粉体粉末冶金協会

キーワード

• PZT
• MnO
• Nb<SUB>2</SUB>O<SUB>5</SUB>
• sintering
• shrinkage

詳細情報

• CRID: 1390282681284584960
• NII論文ID: 10002013118
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.43.1132
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 4036700
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4036700
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可