Preparation of B4C-TiB2 System Composites by Arc Melting and their Thermoelectric Properties.
-
- Goto Takashi
- Institute for Materials Research, Tohoku University
-
- Li Jianhui
- Institute for Materials Research, Tohoku University
-
- Hirai Toshio
- Institute for Materials Research, Tohoku University
Bibliographic Information
- Other Title
-
- 熱電変換材料 アーク溶解法によるB4C‐TiB2系複合セラミックスの作製とその熱電性能
- アーク ヨウカイホウ ニヨル B4C TiB2ケイ フクゴウ セラミックス ノ
Search this article
Abstract
B4C-TiB2 quasi-binary composites were prepared by arc melting in argon atmosphere using B4C and TiB2 powders. Uniform lamella texture indicating eutectic reaction was observed at 25mol%TiB2 in the quasi-binary system. The electrical conductivity of the B4C-TiB2 composites significantly increased with increasing TiB2 content. The thermal conductivity (κ) of the composites containing 2mol%TiB2 was slightly smaller than that of B4C, but the κ values increased with increasing TiB2 content at more than 6mol%. The Seebeck coefficient of B4C-TiB2 composites showed maxima at 6mol%TiB2. The thermoelectric figure-of-merit (Z) values exponentially increased with increasing temperature, showing maxima at 6mol%TiB2. The greatest ZT values obtained in the present study was 0.55 at T=1100K for the composite containing 6mol%TiB2.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 44 (1), 60-64, 1997
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001206306985728
-
- NII Article ID
- 10002013292
-
- NII Book ID
- AN00222724
-
- COI
- 1:CAS:528:DyaK2sXht1aiurw%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 4118700
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed