粉末プロセスの制御と製品評価ＩＩ　放電焼結により固化成形したＦｅ‐ｌ８Ｃｒ‐８Ｎｉ合金の特性と相変化

• 杉山 明

  名古屋工業技術研究所

• 小林 慶三

  名古屋工業技術研究所

• 尾崎 公洋

  名古屋工業技術研究所

• 三輪 謙治

  名古屋工業技術研究所

書誌事項

タイトル別名

• Phase Transformation and Properties of Fe-18Cr-8Ni Alloy Consolidated by Pulse Current Sintering.
• ホウデン ショウケツ ニ ヨリ コカ セイケイシタ Fe 18Cr 8Ni ゴ

抄録

The composition of Fe-18mass%Cr-18mass%Ni alloy powder were prepared by mechanical alloying (MA) of three kinds of elemental powders. The MA powder became homogeneous by milled for 360ks. The hardness of powders MAed after 360ks were about 700Hv. The MA powder was consolidated by pulse current sintering (PCS) method at 1073K. The microstructure of this sample was fine and the hardness was about 400Hv. The sample consolidated by using powders milled in N₂ gas atmosphere contained much y phase. But the sample made by using powders milled in Ar gas atmosphere contained much a phase. Because the phase of powders as MA is almost a, the α -> γ transformation was occurred during heating of sintering. N₂ surpresses the γ ->α transformation during cooling.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 44 (5), 453-457, 1997

  一般社団法人 粉体粉末冶金協会

キーワード

• SUS304
• Fe-18Cr-8Ni
• phase transformation
• N<SUB>2</SUB>
• mechanical alloying
• pulse current sintering

詳細情報

• CRID: 1390282681284095744
• NII論文ID: 10002013828
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.44.453
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 4205766
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4205766
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可