Consolidation of Titanium Tri-aluminide using by Spark Plasma Sintering.
-
- Kobayashi Keizo
- National Industrial Research Institute of Nagoya
-
- Sugiyama Akira
- National Industrial Research Institute of Nagoya
-
- Ozaki Kimihiro
- National Industrial Research Institute of Nagoya
-
- Wen Cui'e
- Beijing University of Aeronautics and Astronautics
Bibliographic Information
- Other Title
-
- 金属間化合物の粉末冶金と諸物性 TiAl3の放電焼結による固化成形
- TiAl3 ノ ホウデン ショウケツ ニヨル コカ セイケイ
Search this article
Abstract
Ti-5mass%Al, Ti-I0mass%A1, Ti-32mass%Al and Ti-64mass%Al were synthesized by mechanical alloying (MA) of Ti powder and Al powder using a planetary ball milling for 360ks in 66kPa argon gas atmosphere. Ti-64mass%Al powder milled for 360ks was Al solid solution. Non stoichiometric Ti-Al powder milled for 360ks became amorphous state with an increase of Al content in the MA powder.<BR>The mixture of MA powder and Al powder, which contained 64mass%Al, was consolidated by spark plasma sintering(SPS). The starting temperature for shrinkage in SPS process was decreased by the addition of Al powder into MA powder. In the mixture of Ti-5mass%Al MA powder and Al powder, the consolidated TiA13 was obtained by SPS at 1073K for 0.3ks. This sintered body had a homogeneous fine microstructure.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 44 (6), 554-559, 1997
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681285367296
-
- NII Article ID
- 10002014054
- 10010465898
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 4228294
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed