湿式加圧成形法を用いたMoSi_2/ZrO_2(2モル%Y_2O_3)系傾斜機能材料の作製 Fabrication of Functionally Graded MoSi_2/ZrO_2 (2mol% Y_2O_3) Materials by Wet-Molding Process

この論文にアクセスする

この論文をさがす

著者

抄録

Functionally graded MoSi<SUB>2</SUB>/ZrO<SUB>2</SUB>(2Y) materials with high density (97.5% of theoretical) have been fabricated by uniaxial wet-molding, followed by hot pressing (1000°C/1h/30MPa) and hot isostatic pressing (1400°C/2h/196MPa). Their composition profiles are much influenced by the viscosity of the mixed solutions of glycerin and ethanol used as dispersion media; a linear compositional gradient from MoSi<SUB>2</SUB>/ZrO<SUB>2</SUB>(2Y)≈70/30 to≈20/80 mol% is obtained from the solution (50/50 vol%) with the viscosity of 20 mPa⋅s. Vickers hardness Hv and fracture toughness K<SUB>Ic</SUB> increase from 9.7 to 12.4 GPa and 5.1 to 12.5 MPa⋅m<SUP>1/2</SUP>, respectively, with increasing ZrO<SUB>2</SUB>(2Y) composition.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 44(6), 565-569, 1997-06-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  14件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  2件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002014079
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4228296
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ