ガラス被覆したPbTeの高温酸化 Oxidation Behavior of Oxidation-resistive Glass-coated PbTe

この論文にアクセスする

この論文をさがす

著者

抄録

Oxidation behavior of lead telluride (PbTe) and glass-coated PbTe was studied at oxygen partial pressures of 10Pa to 0.1MPa in the temperature range between 700 to 900K. Mass loss was observed at moderately low oxygen partial pressures and at high temperatures, while mass gain was observed at high oxygen partial pressures and at low temperatures. For the samples which showed mass loss, Pb<SUB>3</SUB>TeO<SUB>5</SUB> or Pb<SUB>5</SUB>TeO<SUB>7</SUB> formed on the PbTe surface. The formation of PbTeO<SUB>3</SUB> layer or Pb<SUB>2</SUB>TeO<SUB>4</SUB>/PbTeO<SUB>3</SUB> multi-layer caused the mass gain. Oxidation resistance of PbTe was improved by the glass-coating. No mass change was observed up to 20ks.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 44(7), 653-657, 1997-07-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  12件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002014201
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4258096
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ