- Non-shrinkage Alumina Material.
- ム シュウシュク アルミナ ザイリョウ
この論文をさがす
抄録
To fabricate a sintered Al2O3 with high dimensional accuracy by near-net-shape firing, oxidation and sintering behavior of compacts of a mixture of Al2O3 and Al powders was studied. The compacts were prepared by compressing green-sheets obtained by doctor-brade method at 196MPa and fired at 1600°C or less in air. The oxidation of Al in the compact occured between about 450°C and 1300°C, and prevents the compact from shrinking in firing process at 1300°C or less. A part of melting Al in the compact spilled out of the compact in firing process, because Al melts below 800°C, its oxidation temperature. MgO, CaCO3 and TiO2 powders were added to prevent the Al spillage and Si powder was added to prevent the shrinkage by sintering at 1400°C or more. As a result, the sinterd Al2O3 having a density of 3.72g/cm3 and 0.7% shrinkage by sintering was fabricated by sintering with oxidation of Al and formation of mullite.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 44 (8), 729-733, 1997
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681283923456
-
- NII論文ID
- 10002014358
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 4275736
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可