帯域焼鈍法による所望方位を有するMo単結晶の作製 Preparation of Molybdenum Single Crystal with a Desired Orientation by Means of Zone Annealing

この論文にアクセスする

この論文をさがす

著者

抄録

A new technique for preparation of molybdenum single crystal with a desired orientation has been proposed. The technique was performed as follows; first, a specimen with a comb shape was mechanically fabricated from hot-rolled sheet with various rolling procedures and reductions. Then the edge of specimen with a comb shape was locally heated by the optical-beam image furnace in order to make some secondary recrystallized grains with various orientations. After the secondary recrystallized grains were mechanically eliminated except for a secondary grain having a desired orientation, the specimen was zone-annealed at 2000-2200°C at the zone-speed of 5 mm/ hr to grow the secondary grain. Consequently, molybdenum single crystal with a desired crystallographic orientation can easily be produced.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 44(8), 770-774, 1997-08-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  16件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002014433
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4275743
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ