Nd-Fe-B系異方性HDDR処理粉の高保磁力化 Improvement of Intrinsic Coercivity in HDDR-processed Anisotropic Permanent Magnets

この論文にアクセスする

この論文をさがす

著者

抄録

High-coercivity anisotropic magnet powder of H<SUB>cJ</SUB>=1.24MA/m has been developed in HDDR process by substituting Dy for Nd to decrease the value of irreversible thermal flux losses. The newly developed powder provides lower irreversible thermal losses than MQP-B up to 100°C when molded into resin-bonded magnets. The magnets made from the high-HcJ powder give higher relative open flux when magnetized under a magnetization field of 1.2MA/m at 80°C than magnetized at 20°C. To magnetize these magnets at high temperature also decreases the value of irreversible thermal flux losses.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 44(9), 818-821, 1997-09-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  7件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002014526
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4304480
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ