準結晶を含むガス噴霧Al-Cr系合金粉末の押出し成形と機械的性質 Mechanical Properties of Al-Cr Base Alloys Containing Icosahedral Phase Produced by Extrusion of Atomized Powder

この論文にアクセスする

この論文をさがす

著者

抄録

Bulk Al<SUB>96-x</SUB>Cr<SUB>3</SUB>Ce<SUB>1</SUB>Co<SUB>x</SUB>(x=1, 1.5, 2) and Al<SUB>95-x</SUB> Cr<SUB>3</SUB>Ce<SUB>1</SUB>Co<SUB>x</SUB>TM<SUB>1</SUB>(TM=Zr, Mn, Fe) materials with a dimension of about φ8 mm×300 mm were produced by extrusion of gas atomized powders at 523, 573, 623, 673 and 723 K. The gas atomized powder has a spherical shape with an average diameter of about 15μm, which consists of icosahedral, Al, Al<SUB>9</SUB>Co<SUB>2</SUB> and Al<SUB>13</SUB>Cr<SUB>2</SUB> phases. The bulk Al<SUB>94.5</SUB>Cr<SUB>3</SUB>Ce<SUB>1</SUB>Co<SUB>1.5</SUB> material extruded at 573 K consists of icosahedral, Al, Al<SUB>9</SUB>Co<SUB>2</SUB> and Al<SUB>13</SUB>Cr<SUB>2</SUB> phases. The Yong's modulus, Vickers hardness (Hv), ultimate tensile strength and plastic elongation in the bulk form are 83 GPa, 170, 570 MPa and 8.4 % for Al<SUB>94.5</SUB>Cr<SUB>3</SUB>Ce<SUB>1</SUB>Co<SUB>15</SUB> and 89 GPa, 210, 670 MPa and 4.4 % for Al<SUB>93.5</SUB>Cr<SUB>3</SUB>Ce<SUB>1</SUB>Co<SUB>1.5</SUB>Mn<SUB>1</SUB>, respectively. The Hv at the testing temperature of 573 K for the Al<SUB>94.5</SUB>Cr<SUB>3</SUB>Ce<SUB>1</SUB>Co<SUB>1.5</SUB> and Al<SUB>92.5</SUB>Cr<SUB>3</SUB>Ce<SUB>1</SUB>Co<SUB>1.5</SUB>Zr<SUB>2</SUB> bulk materials are 55 and 75, respectively, which are more than twice as large as that for the 7075-T6 alloy.

収録刊行物

  • 粉体および粉末冶金

    粉体および粉末冶金 44(9), 858-863, 1997-09-15

    Japan Society of Powder and Powder Metallurgy

参考文献:  19件中 1-19件 を表示

  • <no title>

    INOUE A.

    J. Mater. Sci. Lett. 6, 194, 1987

    被引用文献9件

  • <no title>

    INOUE A.

    Mater. Trans., JIM 31, 493, 1990

    被引用文献2件

  • <no title>

    KIM Y. H.

    Keikinzoku(J. Jpn. Inst. Lighy Met. ) 42, 217, 1991

    被引用文献1件

  • <no title>

    INOUE A.

    Mater. Trans., JIM 33, 723, 1992

    被引用文献13件

  • <no title>

    INOUE A.

    Mater. Trans., JIM 35, 85, 1994

    被引用文献11件

  • <no title>

    INOUE A.

    Mater. Trans., JIM 36, 1219, 1995

    被引用文献4件

  • <no title>

    KIMURA H. M.

    Mater. Trans., JIM 37, 1722, 1996

    被引用文献3件

  • <no title>

    TAKETANI K.

    J. Mater. Sci. 29, 6513, 1994

    被引用文献4件

  • <no title>

    SHECHTMAN D.

    Phys. Rev. Lett. 53, 1951, 1984

    被引用文献39件

  • <no title>

    MASUMOTO T.

    Trans. Jpn. Inst. Met. 27, 81, 1986

    被引用文献1件

  • <no title>

    INOUE A.

    J. Mat. Sci. 22, 1758, 1987

    被引用文献1件

  • <no title>

    INOUE A.

    Mater. Trans., JIM 33, 723, 1992

    被引用文献13件

  • <no title>

    INOUE A.

    Mater. Trans., JIM 35, 85, 1994

    被引用文献11件

  • <no title>

    INOUE A.

    Meter. Trans. A 19A, 235, 1988

    被引用文献1件

  • <no title>

    ELSER V.

    Phys, Rev, B 32, 4892, 1985

    被引用文献2件

  • <no title>

    岩尾修

    軽金属学会 37, 646, 1987

    被引用文献1件

  • <no title>

    KOBAYASHI K. F.

    Z. Metallkd. 86, 289, 1995

    被引用文献2件

  • <no title>

    上仲秀哉

    日本金属学会会報 36, 104, 1997

    被引用文献2件

  • <no title>

    HORIO Y.

    Mater. Sci. Eng. A179/A180, 596, 1994

    DOI 被引用文献3件

被引用文献:  5件中 1-5件 を表示

各種コード

  • NII論文ID(NAID)
    10002014575
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4304487
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ