ZnOバリスタの低温焼結(850-950℃)のメカニズム Mechanism of Low Temperature Sintering(850-950℃)of ZnO Varistor

この論文にアクセスする

この論文をさがす

著者

抄録

The sintering of ZnO+Bi<SUB>2</SUB>O<SUB>3</SUB>+Sb<SUB>2</SUB>O<SUB>3</SUB> ceramics was studied. Usually, ZnO varistors have been sintered at a temperature higher than 1200°C, because Sb<SUB>2</SUB>O<SUB>3</SUB> in the raw material retards sintering by evaporating at low temperature and forming Sb-compond thin films on ZnO surface. When Bi<SUB>2</SUB>O<SUB>3</SUB> and Sb<SUB>2</SUB>O<SUB>3</SUB> were mixed and heattreated beforehand and added to ZnO, the ZnO+Bi<SUB>2</SUB>O<SUB>3</SUB>+Sb<SUB>2</SUB>O<SUB>3</SUB> could be sintered at about 900°C. During heattreatment with Bi<SUB>2</SUB>O<SUB>3</SUB>, Sb<SUB>2</SUB>O<SUB>3</SUB> reacted with Bi<SUB>2</SUB>O<SUB>3</SUB> and stopped sublimating, and the effect of sintering retardation was disappeared.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 44(12), 1069-1074, 1997-12-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  6件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  3件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002014622
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4380691
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ