Li添加Bi-2212相の生成過程(第2報)-低温生成機構の検討- Formation Process of Li-added Bi-2212 Phase(II)-Formation at a Relatively Low Temperature of 730℃-

この論文にアクセスする

この論文をさがす

著者

抄録

Effects of Li-addition on the formation process of Bi-2212 phase have been studied for samples with a nominal composition of Bi:Sr:Ca:Cu:Li=2:1.5:1.5:2:0.2. Samples were heated at temperatures ranging between 560°C and 730°C in air with various heating rates. The formation range of the phases formed was determined by powder X-ray diffraction method(XRD). Li-addition seems to bring two different effects on the formation process of the Bi-2212 phase: an acceleration of the formation of Bi-2201 phase on heating and early stage of holding at 730°C, and a promotion of phase transformation of Bi-2201 phase to Bi-2212 phase after holding for a few hours. Such two effects can be explained by formation of two different oxides which were newly found. The microstructures of the newly found oxides were observed by scanning electron microscopy(SEM), high-resolution transmission electron microscopy(HR-TEM) and electron diffraction(ED).

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 45(2), 129-134, 1998-02-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  11件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002015030
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4413736
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ