傾斜機能材料　　ペロブスカイト型固溶体Ｋ（Ｔａ，Ｎｂ）Ｏ３の組成傾斜単結晶の合成と誘電特性

• 山根 久典

  東北大学素材工学研究所

• 森田 浩一郎

  東北大学素材工学研究所

• 窪田 俊一

  東北大学素材工学研究所

• 島田 昌彦

  東北大学素材工学研究所

書誌事項

タイトル別名

• Preparation and Dielectric Properties of Composition-Graded K(Ta, Nb)O3 Single Crystals.
• ペロブスカイトガタ コヨウタイ K Ta Nb O3 ノ ソセイ ケイシャ タ

抄録

Single crystals of perovskite-type solid solution, K(Ta_xNb_1-x)O₃, having composition gradient were prepared by non-equilibrium cooling from a melt with the composition x=0.3. The size of the crystals was 1-2 mm. Electron microprobe analysis revealed that Ta content was rich in the core region of the crystals and decreased gradually to the edges with increasing Nb content. The composition gradient depended on cooling procedure. The dielectric constant measured at 500 kHz was in the range from 1000 to 4000 at temperatures from 290 to 720 K. The temperature dependence of dielectric constant reflected the composition gradient in the crystals.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 45 (3), 257-261, 1998

  一般社団法人 粉体粉末冶金協会

キーワード

• functionally graded materials
• perovskite-type structure
• dielectric constant
• single crystal

詳細情報

• CRID: 1390001206307361920
• NII論文ID: 10002015244
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.45.257
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 4447671
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4447671
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可