構成元素間直接反応法により合成したSiC-AlNセラミックアロイ粉焼結体の特性評価 [in Japanese] Preparation of SiC-AlN Ceramic Alloy Powder by Direct Reaction between Constituent Elements and Property Evaluation of its Sintered Compacts [in Japanese]
Access this Article
Search this Article
Fine powders of SiC-A1N ceramic alloy were synthesized by direct reactions of a powder premix of Si, C and Al powders in nitrogen, i.e. Si+C+xAl+(x/2)N<SUB>2</SUB>=SiC:xAIN. The synthesized powders showed a good sinterability; dense compacts were fabricated by hot-isostatic pressing at relatively low temperature (2123K) without additives, or by pressureless sintering with Y<SUB>2</SUB>O<SUB>3</SUB> as a sintering additive. The obtained SiC-A1N alloys showed better mechanical properties than the monolithic SiC and A1N; for example a two to threefold increase in fracture strength was achieved.
- J. Jpn. Soc. Powder Powder Metallurgy
J. Jpn. Soc. Powder Powder Metallurgy 45(4), 316-320, 1998-04-15
Japan Society of Powder and Powder Metallurgy