ニューコンポジット材料　　メカニカルアロイングを用いた微細ＴｉＣ分散合金の作製

• 杉山 明

  名古屋工業技術研究所材料プロセス部

• 小林 慶三

  名古屋工業技術研究所材料プロセス部

• 尾崎 公洋

  名古屋工業技術研究所材料プロセス部

書誌事項

タイトル別名

• Preparation of fine TiC dispersed alloy by mechanical alloying.
• メカニカル アロイング オ モチイタ ビサイ TiC ブンサン ゴウキン ノ

抄録

The formation of ultra fine TiC dispersed alloy by mechanical alloying (MA) and spark plasma sintering (SPS) has been investigated. The composition of Ti_xC_100-x (x=50-80)-20mass%Ni(called cermet) and that of Ti₅₀Ni_x C_50-x (x=20-45) (called NiTi alloy) alloy powder have been synthesized by MA of three kinds of elemental powders. During MA, TiC-Ni consolidation was formed in the vessel for the composition of less than 65at.%Ti mixture. In the case of cermet, after MA, for the composition of more than 70at.% Ti mixture, C and Ni powders were added to MA powder in order to make the total composition of Ti₅₀C₅₀-20mass%Ni cermet. The powder mixture of cermet and NiTi alloy was consolidated by SPS method at 1073K. The size of sintered body was φ15×3mm. This sintered body consisted of TiC, Ni, and Ni-Ti alloy. It was found that the ultra fine TiC (<1000nm) had been formed during SPS process by using Ti₇₅C₂₅-20mass%Ni+C+Ni powder. This ultra fine TiC was dispersed homogeneously in the cermet. In the case of NiTi alloy, the fine TiC was not observed in the sintered sample. And the sample of Ti₅₀Ni_xC_50-x alloy was very brittle.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 45 (4), 341-345, 1998

  一般社団法人 粉体粉末冶金協会

キーワード

• mechanical alloying
• ultra fine TiC
• spark plasma sintering
• cerment
• NiTi

詳細情報

• CRID: 1390001206308854400
• NII論文ID: 10002015453
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.45.341
• COI: 1:CAS:528:DyaK1cXjt1Wqurg%3D
• ISSN: 18809014
• ISSN: 05328799
• ISSN: http://id.crossref.org/issn/05328799
• NDL書誌ID: 4459418
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4459418
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可