• 地引 達弘

  三井造船 (株)

• 田中 正紀

  三井造船 (株)

• 藤原 貴典

  岡山大学地域共同研究センター

• 久谷 益士郎

  三井造船 (株)

書誌事項

タイトル別名

• Improvement of Initial Break-in Condition of Spray Coated Ceramics for Marine Diesel Engine
• ハクヨウ ディーゼル キカン ニ オケル セラミックス ヨウシャ ヒマク ノ

抄録

The partial contacting wear test of spray coated ceramics was carried out by using pin-on-disk type wear testing machine. The test results of spray coated ceramics with no treatment were compared with that of Ni-P + PTFE plated spray coated ceramics. And observation of wear surface was carried out using together some methods of observation in order to analyze the wear surface in initial break-in condition quantitatively.<BR>The main results are in the following : Spray coated ceramics was worn abnormally after partial contacting wear test, but Ni-P + PTFE plated spray coated ceramics was worn normally, protecting from the damage by partial contacting. Phenomenon of surface break-in condition can be evaluated quantitatively by statistical treatment of wear surface profile.

収録刊行物

• 日本舶用機関学会誌

  日本舶用機関学会誌 32 (12), 904-914, 1997

  公益社団法人 日本マリンエンジニアリング学会

詳細情報

• CRID: 1390001205161219328
• NII論文ID: 10002041884
• NII書誌ID: AN00196373
• DOI: 10.5988/jime1966.32.904
• ISSN: 18844758
• ISSN: 03883051
• NDL書誌ID: 4353327
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4353327
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可