アーク溶解および熱処理により作製したSiB_<14>-SiB_6系複合セラミックスの熱電性能 Thermoelectric Properties of SiB_<14>-SiB_6 Composites Prepared by Arc Melting and Annealing

この論文にアクセスする

この論文をさがす

著者

抄録

Si-B system composites were prepared by arc melting using Si and B powders and then annealed in an argon atmosphere. Arc-melted specimens consisted of mainly SiB<SUB>14</SUB> and free Si. SiB<SUB>6</SUB> phase formed at the boundary between SiB<SUB>14</SUB> and free Si at content of 80 to 86mo1%B by the annealing at 1670K. The lattice parameter of SiB<SUB>14</SUB> increased with increasing annealing time due to the change of Si to B content ratio in SiB<SUB>14</SUB> phase. The electrical and thermal conductivity of the composites decreased with increasing annealing time, but the Seebeck coefficient (α) showed maxima at the annealing time around 5.4ks. The greatest dimensionless figure-of-merit (ZT) value obtained in this study was 0.14 at T=1100K.

収録刊行物

  • 粉体および粉末冶金

    粉体および粉末冶金 45(6), 581-585, 1998-06-15

    Japan Society of Powder and Powder Metallurgy

参考文献:  14件中 1-14件 を表示

  • <no title>

    FELGELSON R. S.

    Ceram, Bull. 42, 688-693, 1963

    被引用文献1件

  • Novel Refractory Semiconductor

    WOOD C.

    Materials Research Society Symposia Proceedings 97, 33, 1987

    被引用文献1件

  • <no title>

    BEREZIN A. A.

    Sov. Phys. Solid State 15, 1237-1239, 1973

    被引用文献1件

  • <no title>

    CHEN L.

    Proc. 16th Int. Conf. Thermoelectrics 215, 1997

    被引用文献1件

  • Novel Refractory Semiconductor

    ASELAGE T. L.

    Materials Research Society Symposia Proceedings 97, 27, 1987

    被引用文献1件

  • Novel Refractory Semiconductor

    WOOD C.

    Materials Research Society Symposia Proceedings 97, 335, 1987

    被引用文献1件

  • シリコンボライドの熱電特性に及ぼす相組成および微細構造の影響

    陳 立東 , 後藤 孝 , 李 剣輝 , 新野 正之 , 平井 敏雄

    電気学会論文誌. A, 基礎・材料・共通部門誌 = The transactions of the Institute of Electrical Engineers of Japan. A, A publication of Fundamentals and Materials Society 116(3), 248-252, 1996-03

    参考文献13件 被引用文献2件

  • <no title>

    RIZZO H. F.

    J. Am. Ceram. Soc. 43, 550-552, 1960

    DOI 被引用文献1件

  • <no title>

    VLASSE M.

    J.Solid State Chem. 37, 181-188, 1981

    被引用文献3件

  • <no title>

    ARMAS B.

    J. Less Com. Met. 82, 245-254, 1981

    被引用文献3件

  • <no title>

    MUKAIDA M.

    Mater. & Manufacturing Processes 7, 625-647, 1992

    DOI 被引用文献1件

  • <no title>

    ARMAS B.

    J.Less-Common Met. 47, 135-140, 1976

    被引用文献4件

  • <no title>

    OLESINSKI R. W.

    Bull.Alloy Phase Diagrams 5, 478-484, 1984

    DOI 被引用文献11件

  • <no title>

    MAGNUSSON B.

    Acta. Chem. Scand 16, 449-455, 1962

    DOI 被引用文献1件

各種コード

  • NII論文ID(NAID)
    10002052284
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4502283
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ