Hot Isostatic Pressing of Y_2O_3-Doped La_2Zr_2O_7 Prepared by the Hydrazine Method

この論文にアクセスする

この論文をさがす

著者

抄録

Pyrochlore La<SUB>2</SUB>Zr<SUB>2</SUB>O<SUB>7</SUB> containing 8 mol% Y<SUB>2</SUB>O<SUB>3</SUB> crystallizes at 825°to 885°C from an amorphous material prepared by the hydrazine method. The lattice parameter is α=1.0751 nm; this value is smaller than that (α=1.0793 nm) of pure La<SUB>2</SUB>Zr<SUB>2</SUB>O<SUB>7</SUB>. Dense Y<SUB>2</SUB>O<SUB>3</SUB>-doped La<SUB>2</SUB>Zr<SUB>2</SUB>O<SUB>7</SUB> ceramics (99.7% of theoretical) with an average grain size of 3.8 μm have been fabricated by hot isostatic pressing for 2 h at 1500°C and 196 MPa. They exhibit electrical conductivity of 1.6 S⋅m<SUP>-1</SUP> at 1000°C. Activation energies are 0.82 and 0.58 eV for initial (400°-540°C) and final (540°-1000°C) stages, respectively.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 45(6), 586-589, 1998-06-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  11件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002052299
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4502284
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ