放電プラズマ焼結法によるステライトの固化成形およびステンレス鋼との接合 Consolidation of Stellite and Its Bonding to Stainless Steel by Spark Plasma Sintering

この論文にアクセスする

この論文をさがす

著者

抄録

Spark plasma sintering (SPS) was applied to consolidating Stellite powder and bonding Stellite to stainless steel. Sintered compacts with relative densities more than 99.5 % were obtained by the SPS conditions, applied pressure=50 MPa, heating rate=50°C min<SUP>-1</SUP>, sintering temperature=1070°C and holding time=l0 min. They have good mechanical properties due to their finely-dispersed structures of carbide particles. Stellite and stainless steel could be easily bonded by SPS of Stellite powder placed on rod like stainless steel under the same conditions as the consolidation of Stellite powder. Diffusion zones in junctions were very narrow because of short-time and low-temperature sintering.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 45(7), 675-679, 1998-07-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  6件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002052470
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4535716
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ