焼結接合法によるフェライト部品の作製 Sinter Joining Properties of Ferrite Magnets

この論文にアクセスする

この論文をさがす

著者

抄録

For the purpose of fabricating ferrite part with a complicated shape which has different orientation of the ferrite, joining of pre-formed green compacts was studied, and in particular the feasibility of combined sinter joining method was investigated. As the first step, two simple compacts of disk and ring shape have been individually produced under the non-magnetic field condition. The two compacts was assembled into a unit and then sintered at 1150°C and 1225°C. Effect of addition agent and sintering temperature on the joint strength of the the sintered compacts has been studied. The joint strength of the compacts sintered at 1225°C was about 2 times of that of the compacts sintered at 1150°C. The maximum joint strength was obtained when an inner disk with 0.75mass%CaO and an outer ring with 0.75mass%CuO was joined at sintering temperature of 1225°C.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 45(8), 763-768, 1998-08-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  7件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  6件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002052631
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4540070
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ