Mechanical alloying process of Al-Ti-B powder mixture and its heat treatment property.
-
- Yuasa Eiji
- Musashi Institute of Technology
-
- Kawamura Chuji
- Musashi Institute of Technology
-
- Tamura Masaomi
- Graduate School Musashi Institute of Technology
Bibliographic Information
- Other Title
-
- メカニカルアロイングしたAl‐Ti‐B粉末の合金化過程とその熱処理特性
- メカニカル アロイング シタ Al-Ti-B フンマツ ノ ゴウキンカ カテイ
Search this article
Abstract
Titanium and boron powders were mixed with various contents of molar ratio Ti/B=1/2 to aluminum powder and then the mixture was mechanically alloyed for various milling times. Aluminum phase super-saturated with titanium and boron is formed by the mechanical alloying for belonged milling time and the crystalline size of α-Al phase in the powder particle with high Ti/B content becomes to nanometer order. Vickers hardness of the mechanically alloyed powder particles increases with milling time and of Ti/B contents. Al-5mass%Ti and Al-20mass% (Ti/B) powders mechanically alloyed for 108ks were heat-treated for various times at 723-873K in argon atmosphere. When the Al-20mass%(Ti/B) powder was heat-treated at temperature range of 723-823K, the age-hardening phenomenon occurs and Vickers hardness of the particles becomes to higher.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 45 (10), 990-994, 1998
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681285895552
-
- NII Article ID
- 10002053074
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 4585468
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed