Hot Isostatic Pressing of SnO2 Prepared by the Hydrazine Method (特集 ナノ構造制御と新機能発現) Hot Isostatic Pressing of SnO_2 Prepared by the Hydrazine Method

この論文にアクセスする

この論文をさがす

著者

抄録

Reactive Snot powders have been prepared by the hydrazine method. Their individual particles tend toward a hexagonal morphology with increasing temperature. Well-densified SnO<SUB>2</SUB> ceramics (99.8% of theoretical) with an average grain size of 0.9μm have been fabricated by hot isostatic pressing for 2 h at 900°C and 196 MPa. Their Vickers hardness and bending strength are -14.4 GPa and -200 MPa, respectively. They exhibit an electrical conductivity of -5 × 10<SUB>-3</SUB> S⋅cm<SUP>-1</SUP> at room temperature.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 45(12), 1157-1161, 1998-12-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  14件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002053404
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4629452
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ