磁石・磁性材料の化学　Ｉ　　Ｓｒフェライト粉末を用いたボンド磁石の磁気特性に及ぼす成形条件の影響

• 細川 誠一

  住友特殊金属(株)

• 豊田 幸夫

  住友特殊金属(株)

• 沖本 邦郎

  摂南大学工学部

• 和泉 克尚

  摂南大学大学院工学研究科

書誌事項

タイトル別名

• The Influence of the Molding Condition on Magnetic Properties of Bonded Magnets with Sr-Ferrite Powders.
• Sr フェライト フンマツ オ モチイタ ボンド ジシャク ノ ジキ トクセイ ニ オヨボス セイケイ ジョウケン ノ エイキョウ

抄録

The influences of the molding pressure (30, 50MPa) and temperature (100-250°C) on magnetic properties of bonded magnets with Sr-ferrite powders are investigated. The coercivity of the bonded magnets is almost constant 240kAm-1 at the molding temperature of about 200°C or more and independent of molding pressure. The reason why the coercivity of bonded magnets scarcely reduced during molding is due to quasi-isostatic pressure applied for Sr-ferrite powders by resin among the powders, considered by experiments using CIP and powder epoxy resin. The reduction of coercivity of Sr-ferrite powders is caused by mixing the compound. And the reduction of coercivity corresponds with mixing torque, which relates to shapes of Sr-ferrite powders.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 46 (1), 72-76, 1999

  一般社団法人 粉体粉末冶金協会

キーワード

• Sr-ferrite
• bonded magnest
• isostatic pressing
• mixing torque

詳細情報

• CRID: 1390001206307182592
• NII論文ID: 10002053652
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.46.72
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 4639986
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4639986
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可