Morphology on the Surface of Wool Fibers Treated with Glow Discharge under Atmospheric Pressure.
-
- Nakashima Yoichi
- Technology Research Institute of Osaka Prefecture
-
- Tahara Mitsuru
- Technology Research Institute of Osaka Prefecture
-
- Kimura Hirokazu
- Technology Research Institute of Osaka Prefecture
-
- Takagishi Toru
- Department of Applied Materials Science, Osaka Prefecture University
書誌事項
- タイトル別名
-
- Morphology on the Surface of Wool Fiber
この論文をさがす
抄録
The surface structures of wool fibers treated with the glow discharge under atmospheric pressure and the low-temperature plasma were mainly examined by SEM. The ruggedness morphologies, which were caused by the oxidation-etching effects, were observed on the surface of specimens treated with oxygen low-temperature plasma. The morphology of the specimens treated with low-temperature plasma of helium gas flow was little changed compared with original one. In the case of glow discharge under atmospheric pressure, numerous granules with a diameter of ca. 0.15μm appeared on the cuticle layer. These granules were completely soluble in methanol. According to the XPS spectra, such granular materials consist of substances containing large amount of carboxyl group. It was suggested that such granules were composed of polar compounds with lower-molecular weight which were different from the original substance of wool fiber. It is likely that the granular materials are degraded products of the proteins in surface layer generated partly by the glow-discharge energy and remained on the surface of wool fibers due to the atmospheric pressure.
収録刊行物
-
- 繊維学会誌
-
繊維学会誌 54 (10), 496-501, 1998
社団法人 繊維学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204830464384
-
- NII論文ID
- 130004074993
- 10002060257
-
- NII書誌ID
- AN00131651
-
- ISSN
- 18842259
- 00379875
-
- NDL書誌ID
- 4585027
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可