Strain-hardening Property and Internal Deformation of Polymer Composite Melts under Uniaxial Elongation.
-
- Takahashi Tatsuhiro
- Department of Materials Science and Engineering, Yamagata University
-
- Nakajima Hirokazu
- Department of Materials Science and Engineering, Yamagata University
-
- Masubuchi Yuichi
- Department of Materials Science and Engineering, Yamagata University
-
- Takimoto Jun-ichi
- Department of Materials Science and Engineering, Yamagata University
-
- Koyama Kiyohito
- Department of Materials Science and Engineering, Yamagata University
書誌事項
- タイトル別名
-
- Strain-hardening Property and Internal
この論文をさがす
抄録
Uniaxial elongational viscosity of low density polyethylene (LDPE) gave the strain-hardening property. However, talc-filled LDPE showed almost no strain-hardening property and glass-fiber-filled LDPE exhibited the strain-softening property. The cause of almost no strain-hardening property or strain-softening property was discussed from flow observation of internal deformation using visual model experiments. Silicone gums including a glass bead or a glass fiber with a black silicone gum marker were elongated. The internal strain in a glass-bead-filled system was larger than the external strain along the elongational axis, and the received internal strain was larger around a particle than far way from a particle. The internal strain in a glass-fiber-filled system did not depend on the location when the initial orientation of the fiber was perpendicular to the elongational direction. While, the received internal strain next to the fiber without the both edges was almost none when the initial fiber was parallel to the elongational direction. Nonuniformities of internal flow by the addition of fillers seem to be associated with no strain-hardening property or strain-softening property.
収録刊行物
-
- 繊維学会誌
-
繊維学会誌 54 (10), 538-543, 1998
社団法人 繊維学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679807156864
-
- NII論文ID
- 130004075002
- 10002060374
-
- NII書誌ID
- AN00131651
-
- COI
- 1:CAS:528:DyaK1cXntVKkt74%3D
-
- ISSN
- 18842259
- 00379875
- http://id.crossref.org/issn/00379875
-
- NDL書誌ID
- 4585036
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可