Processing High-Level Liquid Waste by Super-High-Temperature Method,(3)Reactions of Platinum Metal Oxides with Titanium Nitride

DOI Web Site 参考文献13件
  • UNO Masayosi
    Department of Nuclear Engineering, Faculty of Engineering, Osaka University
  • KADOTANI Youji
    Department of Nuclear Engineering, Faculty of Engineering, Osaka University Nippon Electric Glass Company
  • MIYAKE Chie
    Department of Nuclear Engineering, Faculty of Engineering, Osaka University Osaka Institute of Technology
  • HORIE Misato
    Power Reactor and Nuclear Fuel Development Corporation

書誌事項

タイトル別名
  • Processing High-Level Liquid Waste by Super-High-Temperature Method, (III).
  • Processing High-Level Liquid Waste by S
  • Reactions of Platinum Metal Oxides with Titanium Nitride

この論文をさがす

抄録

The process constituting the elements of the method for treating high-level liquid waste with addition of reducing agent at temperatures above 1, 873K were examined applying thermogravimetry and X-ray diffractometry to sample mixtures of the platinum metal oxides RuO2, Rh2O3, PdO and of Re2O7, with and without addition of TiN as reducing agent. The addition of TiN reducing agent proved to induce reduction of the platinum metal oxides at temperatures far below those of thermal decomposition occurring in the absence of reducing agent. The presence of reducing agent further proved to reduce Re2O7 to ReO3 at 373K, to ReO2 at 773K and to Re metal at 1, 073K. At around 773K disproportionation reconverted part of the ReO3 formed at 373K to ReO2 and Re2O7. Thus, sublimation of the Re2O7 in starting material which occurs at 523K in the absence of TiN was eliminated, and occurred only at 773K on the Re2O7 that was regenerated at that temperature by disproportionation of the converted ReO3. Alloys of Ru, Rh and Pd resulting from the above treatment with TiN proved to agree with what is indicated from phase diagrams. Among the alternative compounds existing in the Rh-Ti and Rh-Ti binary systems, however, solely Ru-Ti proved to have been produced.