Corrosion Behavior of Stainless Steel in Nitric Acid Solution under Gamma-ray Irradiation.
-
- NAGAI Takayuki
- Tokai Works Power Reactor and Nuclear Fuel Development Corporation
-
- TAKEUCHI Masayuki
- Tokai Works Power Reactor and Nuclear Fuel Development Corporation
-
- TAKEDA Seiichiro
- Tokai Works Power Reactor and Nuclear Fuel Development Corporation
-
- YAMAMOTO Takao A.
- Department of Nuclear Engineering Osaka University
-
- TSUKUI Shigeki
- Research Institute for Advanced Science and Technology Osaka Prefecture University
-
- OKAMOTO Shinichi
- Research Institute for Advanced Science and Technology Osaka Prefecture University
Bibliographic Information
- Other Title
-
- Corrosion Behavior of Stainless Steel i
Search this article
Abstract
Influence of the irradiation on the corrosion behavior of stainless steel (type 304ULC) in boiling nitric acid solution was examined by using 60Co γ-ray source. It was found from the experimental results that radiolysis products of nitric acid (NOχ, HNO2) resulted from the γ-ray irradiation made the environment in the bulk solution more reducing one. On the other hand, corrosion rate of 304ULC was slightly enhanced by the irradiation, which being trivial from the engineering viewpoint. From the result of an AC impedance measurement, this corrosion enhancement was inferred as caused by an enhancement in the current across the passive film by the γ-ray irradiation on the stainless steel surfaces.
Journal
-
- Journal of Nuclear Science and Technology
-
Journal of Nuclear Science and Technology 35 (7), 502-507, 1998
Atomic Energy Society of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204096252672
-
- NII Article ID
- 10002079754
-
- NII Book ID
- AA00703720
-
- COI
- 1:CAS:528:DyaK1cXls1CrsLs%3D
-
- ISSN
- 18811248
- 00223131
-
- NDL BIB ID
- 4525687
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed