硫酸浴からのＺｎ‐Ｃｏ‐シリカ複合めっきに及ぼす界面活性剤の影響

• 日野 実

  岡山県工業技術センター

• 西田 典秀

  岡山県工業技術センター

• 平松 実

  岡山県工業技術センター

• 久我 久徳

  岡山理科大学 現: (株) 太陽

• 金谷 照人

  岡山理科大学工学部

書誌事項

タイトル別名

• Surfactant Influence on Zn-Co-SiO2 Composite Plating from Sulfate Solutions.
• リュウサンヨク カラ ノ Zn Co シリカ フクゴウ メッキ ニ オヨボス

抄録

In response to growing needs for improved corrosion resistance in the steel parts of automobiles and aircraft, plating with Zn-based alloys is being applied in place of pure Zn plating. Zn-based composite plating is also expected to exhibit better corrosion resistance than pure Zn or Zn-alloy plating due to the existence of dispersed particles.<br>Experiments were undertaken to determine the dependence of Zn-Co-SiO₂ composite plating electrodeposition and surface morphology from sulfate solutions on surfactants.<br>We found that the SiO₂ content of deposits without surfactants increased with SiO₂ concentration in the bath, but not for those with surfactants. The SiO₂ content depended on the SiO₂ concentration and the cathode current density. Despite identical plating conditions, surfactant addition is lowered the deposit's Co content and greatly affected the crystal structure and surface morphology.

収録刊行物

• 表面技術

  表面技術 49 (4), 407-411, 1998

  一般社団法人 表面技術協会

キーワード

• Electrodepositions
• Zn-Co-SiO₂ Composite Plating
• Surfactants

詳細情報

• CRID: 1390282679092442624
• NII論文ID: 10002109196
• NII書誌ID: AN1005202X
• DOI: 10.4139/sfj.49.407
• COI: 1:CAS:528:DyaK1cXitFCktrk%3D
• ISSN: 18843409
• ISSN: 09151869
• ISSN: http://id.crossref.org/issn/09151869
• NDL書誌ID: 4447695
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4447695
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可