光沢Ni-Crめっき鋼板の屋外暴露試験による腐食特性についての統計的評価 Statistical Evaluation of Corrosion Characterisitcs of Bright Ni-Cr Electroplated Steel Panels Subjected to the Outdoor Exposure Test

この論文にアクセスする

この論文をさがす

著者

抄録

Corrosion characteristics of a bright Ni-Cr electroplating system on steel were statistically evaluated. For three thicknesses of Ni, a set of fifteen panels was subjected to outdoor exposure tests. Variation in the corrosion characteristics was based on a probabilistic feature, and may be caused by electrochemical noise and nonequilibrium fluctuations. The time to failure for each panel was estimated from the smoothed curves of the percent area of corrosion. To sample life distribution of individual Ni thicknesses, a Weibull distribution was fitted. The failure mode of the bright Ni-Cr electroplating system was wear-out type of failure. The maximum service life, B<sub>10</sub> life, increased logarithmically with increasing Ni thickness.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan

    表面技術 = The Journal of the Surface Finishing Society of Japan 49(6), 632-636, 1998-06-01

    The Surface Finishing Society of Japan

参考文献:  11件中 1-11件 を表示

  • <no title>

    藤田実

    表面技術 48, 201, 1997

    被引用文献1件

  • <no title>

    MARTIN J. W.

    J. Coatings Technology 57(724), 31, 1985

    被引用文献2件

  • <no title>

    MARTIN J. W.

    J. Coatings Technology 57(724), 39, 1985

    被引用文献1件

  • <no title>

    MARTIN J. W.

    J. Coatings Technology 57(724), 49, 1985

    被引用文献1件

  • <no title>

    増子昇

    21, 347, 1983

    被引用文献1件

  • <no title>

    FUJITA M.

    Proc. Am. Electrochemical. Soc. PV 92-23, 199, 1992

    被引用文献2件

  • <no title>

    渡辺徹

    金属表面技術 37, 440, 1986

    被引用文献5件

  • <no title>

    橘孝二

    表面技術 45, 979, 1994

    被引用文献2件

  • <no title>

    青柿良一

    材料と環境 43, 45, 1994

    被引用文献2件

  • <no title>

    藤田実

    表面技術 45, 958, 1994

    被引用文献2件

  • <no title>

    FRANSAER J.

    J. Electrochem. Soc. 142, 4181, 1995

    DOI 被引用文献2件

各種コード

  • NII論文ID(NAID)
    10002109633
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    4502332
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ