接触めっき法によるFe-B二元系アモルファス合金薄膜の作製と磁気特性 [in Japanese] Fabrication of Amorphous Fe-B Alloy Films by Contact Plating Method and Their Magnetic Properties [in Japanese]
Access this Article
Search this Article
Fe-B amorphous alloy film was formed by means of contact plating method, in which Cu foils in contact with Al wires were used as substrates. Local battery configuration of the Cu foil anode and the Al wire cathode was responsible for film formation. The boron content in film was controlled from 0at% to 28at% by changing the KBH<sub>4</sub> concentration in the bath. The bath temperature strongly affected the crystallographic structure of resultant films. Fe<sub>80</sub>B<sub>20</sub> amorphous films required a bath temperature below 40°C. Film structure and composition also affected magnetic properties. Film coercivity below 17Oe was also observed.
- Jitsumu Hyomen Gijutsu
Jitsumu Hyomen Gijutsu 49(7), 769-774, 1998-07-01
The Surface Finishing Society of Japan