高温濃厚LiBr水溶液中における炭素鋼とロウ材との異種金属間腐食 Galvanic Corrosion between Carbon Steel and Soldering Fluxes in a Concentrated LiBr Solution at High Temperatures

この論文にアクセスする

この論文をさがす

著者

抄録

Galvanic corrosion between carbon steel and soldering fluxes was studied in a concentrated LiBr solution at 383 and 433K, using extreme-value statistical analysis of pit depth in soldered parts, measurement of the amount of dissolved Fe<sup>2+</sup> and dissolved flux compornents, and corrosion potential and galvanic current measurement. The soldering fluxes used were copper, copper alloys (Cu-Si-Mn, BAg-8, Ag 30-Cu, 70/30 Cupronickle) and nickel.<br>Nickel flux soldered with carbon steel caused considerable galvanic corrosion of carbon steel at 383K, while carbon steel soldered with copper and copper alloy fluxes showed galvanic corrosion of the fluxes at 383 and 433K. The galvanic corrosion rate of fluxes decreased in the order of copper>Cu-Si-Mn>Ag 30-Cu>BAg-8> 70/30 cupronickel at 433K, and Cu-Si-Mn>copper>Ag 30-Cu>BAg-8>70/30 cupronickel at 388K. 70/30 cupronickel flux was considered the most suitable soldering flux in a concentrated LiBr solution at high temperature.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan  

    表面技術 = The Journal of the Surface Finishing Society of Japan 49(8), 875-880, 1998-08-01 

    The Surface Finishing Society of Japan

参考文献:  6件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002110284
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    4546111
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ