ZrO_2-NiCrAlYプラズマ溶射皮膜の熱応力によるき裂の特性 Crack Property Due to Thermal Stress for ZrO_2-NiCrAlY Plasma Sprayed Layer

この論文にアクセスする

この論文をさがす

著者

抄録

We studied the expanding and reducing of cracks in thermal cycling such as heating and cooling for the ZrO<sub>2</sub>+8%Y<sub>2</sub>O<sub>3</sub> layer built up from plasma spray on stainless steel and carbon steel, with the following Results<br>1) The ZrO<sub>2</sub>+8%Y<sub>2</sub>O<sub>3</sub> layer showed self-repair in thermal cycling such as heating and cooling.<br>2) The ZrO<sub>2</sub>+8%Y<sub>2</sub>O<sub>3</sub> layer sprayed on carbon steel had better self-repair than that sprayed on stainless steel, indicating that ZrO<sub>2</sub>+8%Y<sub>2</sub>O<sub>3</sub> layer self-repair was influenced by a substrate's expansion coefficient.<br>3) Self-repair of the ZrO<sub>2</sub>+8%Y<sub>2</sub>O<sub>3</sub> layer is the characteristic property of ZrO<sub>2</sub>+8%Y<sub>2</sub>O<sub>3</sub> layer built up by spraying particles.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan  

    表面技術 = The Journal of the Surface Finishing Society of Japan 49(10), 1100-1104, 1998-10-01 

    The Surface Finishing Society of Japan

参考文献:  9件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002110848
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    4579095
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ