Electrodeposition of Amorphous Co-Zn Alloy from Ambient-Temperature Molten Salt Electrolytes of EMIC System.
-
- KOURA Nobuyuki
- Fac. of Science & Technology, Tokyo Univ. of Science
-
- MATSUMOTO Satoshi
- Fac. of Science & Technology, Tokyo Univ. of Science
-
- IDEMOTO Yasushi
- Fac. of Science & Technology, Tokyo Univ. of Science
Bibliographic Information
- Other Title
-
- EMIC系常温型溶融塩浴からの非晶質Co‐Zn合金の電析
- EMICケイ ジョウオンガタ ヨウユウエンヨク カラ ノ ヒショウシツ Co-
Search this article
Abstract
A Co-Zn alloy deposit was obtained from ambient temperature molten salt electrolyte CoCl2-ZnCl2-EMIC. The Co content in the Co-Zn alloy deposit was continuously controlled from 0 to 100wt% by controlling the bath composition and current density. Co-Zn alloy deposit morphology was significantly improved by EMIC. Moreover, the bath temperature could be decreased from 130 to 80°C. The Co-Zn alloy deposit crystal structure changes from the Zn binary phase and intermetallic compound Co5Zn21 to the Co binary phase and the intermetallic corresponding compound as a function of Co content in the deposit. An amorphous deposit of Co-Zn alloy is obtained from this molten electrolyte.
Journal
-
- Journal of The Surface Finishing Society of Japan
-
Journal of The Surface Finishing Society of Japan 49 (11), 1215-1219, 1998
The Surface Finishing Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679090764672
-
- NII Article ID
- 10002111081
-
- NII Book ID
- AN1005202X
-
- COI
- 1:CAS:528:DyaK1cXnsFyqtrs%3D
-
- ISSN
- 18843409
- 09151869
- http://id.crossref.org/issn/09151869
-
- NDL BIB ID
- 4603785
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed