ラジウムめっきリードフレームの曲げ特性に及ぼす下地ニッケルめっきの析出条件の影響 Influence of Nickel Plating Uuderlayer Deposition Conditions on Bending Characteristics of Palladium Plating Leadframe

この論文にアクセスする

この論文をさがす

著者

抄録

In the palladium plating leadframe, nickel and palladium are plated over the whole surface including outerleads in the leadframe manufacturing process. Users have pointed out plating film cracks after bending of outerleads. The most thickness of the plating film is nickel.<br>We changed nickel plating conditions and studied the influence on plating film cracks, with the following results: (1) Nickel plating film from a sulfamate bath produces fewer cracks than that from a Watt's bath and is suitable for the underlayer of palladium plating film. (2) Internal stress in nickel plating film rises abruptly when the sulfamate bath pH exceeds 5.0. Even then, cracks did not grow larger, indicating no correlation between internal stress and crack extent. (3) Plating conditions should be monitored to maintain plating thickness because current efficiency changes with plating conditions. Their influence on cracks is small.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan

    表面技術 = The Journal of the Surface Finishing Society of Japan 49(12), 1283-1290, 1998-12-01

    The Surface Finishing Society of Japan

参考文献:  8件中 1-8件 を表示

  • <no title>

    GRANITZ D. A.

    Electron. Pack. Proc. 117, 1982

    被引用文献1件

  • <no title>

    ABBOTT D. C.

    Int. Electron. Pack. Conf. TS-02-6, 1990

    被引用文献1件

  • <no title>

    SCHETTY R.

    Proc. AESF. Annu. Tech. Conf. 83rd 449, 1996

    被引用文献1件

  • <no title>

    珍田聡

    表面技術 44, 1154, 1993

    被引用文献1件

  • <no title>

    珍田聡

    日立電線 17, 97, 1998

    被引用文献1件

  • <no title>

    CHINDA A.

    Hitachi Cable Review 17, 57, 1998

    被引用文献1件

  • <no title>

    珍田聡

    表面技術 45, 691, 1994

    被引用文献2件

  • <no title>

    日本プレーティング協会編

    実用めっき(I) 197, 1983

    被引用文献1件

各種コード

  • NII論文ID(NAID)
    10002111225
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    4624035
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ