燃焼合成による球状黒鉛鋳鉄基板へのNi-Al系金属間化合物コーティング層の生成 Fabrication of Ni-Al Intermetallic Compound Layer on Spheroidal Graphite Cast Iron Substrate by SHS Reaction

この論文にアクセスする

この論文をさがす

著者

抄録

  The coating layers of Ni-Al Intermetallic compounds were prepared on spheroidal graphite cast iron substrates by the applying of self-propagating high-temperature synthesis (SHS) reaction, and simultaneously bonded on substrates by the excessive heat of reaction. The results obtained were as follows. (1) The synthesizing reactions begin at about 873K before the melting point of Al. (2) The reaction layer consists of Ni<sub>3</sub>Al, NiAl, Ni<sub>2</sub>Al<sub>3</sub> and Ni phases, and it sufficiently bonded on base metal. (3) With the powder compact of Ni-60 at % Al, Ni solid solution almost disappeared in the reaction layer, and then the hardest phase, Ni<sub>2</sub>Al<sub>3</sub> of Ni-Al intermetallic compounds was produced.

収録刊行物

  • 鋳造工学 = Journal of Japan Foundry Engineering Society  

    鋳造工学 = Journal of Japan Foundry Engineering Society 68(5), 417-422, 1996-05-25 

    Japan Foundry Engineering Society

参考文献:  9件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002113498
  • NII書誌ID(NCID)
    AN10514770
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    13420429
  • NDL 記事登録ID
    3976365
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-277
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ