球状黒鉛鋳鉄基板におけるNi-Al系金属間化合物被覆層の緻密化 Densification of Ni-Al Intermetallic Coating on Spheroidal Graphite Cast Iron Substrate

この論文にアクセスする

この論文をさがす

著者

抄録

  To examine the adequacy of densified Ni-Al intermetallic coatings as a surface modification process, the intermetallic compound by SHS reaction was coated on a spheroidal graphite cast iron substrate. The results obtained are that the void ratio in reaction layer after SHS reaction decreases with increasing pressure at cold pressing in the preparation of powder compact and pressure at hot pressing. Secondly the bondings between reaction layer and substrate are sufficiently achieved at all the conditions without compressing at hot pressing, but the conversion of SHS reaction layer to full densification is incomplete.

収録刊行物

  • 鋳造工学 = Journal of Japan Foundry Engineering Society  

    鋳造工学 = Journal of Japan Foundry Engineering Society 68(10), 852-857, 1996-10-25 

    Japan Foundry Engineering Society

参考文献:  5件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002114053
  • NII書誌ID(NCID)
    AN10514770
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    13420429
  • NDL 記事登録ID
    4057333
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-277
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ