マグネシウムダイカストAZ91Dの化成処理により成長した表面皮膜の構造と生成機構 Structure and Formation Mechanism of Surface Films Formed on Magnesium Die Cast AZ91D by Chemical Conversion Coating

この論文にアクセスする

この論文をさがす

著者

抄録

The structure and the formation mechanism of surface oxide films grown on magnesium die cast AZ91D have been studied. The substrate surface after chemical etching shows grains of Mg solid solution matrix of several μm in size with Mg<sub>17</sub>Al<sub>12</sub> compound at grain boundaries, large and small voids, and cavities between the grains. The film surface after chemical conversion coating has a granular structure, with each granule corresponding to a single grain. Direct cross sectional observation revealed that the film was formed by anodic reaction and had a porous cell structure which was separated from the substrate by a thin barrier layer at the film/metal interface. The porous film is composed of cell colonies in the sub-micron range that have branched fine pores, with central holes (mother pores) sized approximately 50nm. Square shaped holes about 300nm in size observed on the film surface are believed to be cathodic sites.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan  

    表面技術 = The Journal of the Surface Finishing Society of Japan 47(3), 263-267, 1996-03 

    The Surface Finishing Society of Japan

参考文献:  19件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002255914
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    3936741
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ